HDPE made via Spherilene Gas-Phase Technology
52505 is a HDPE copolymer which is manufactured in gas phase process. This grade is an injection molding grade for applications requiring a good physical property even at low temperatures, like pails, containers and technical moldings.
HDPE: HD52505| HD62505UV
Characteristic Properties
Good Physical Property even at low temperatures
Density: 0.950-0.954
Main Applications
Caps and closures for mineral water bottles
Caps for sparkling water and carbonated soft drinks, beverage caps.
Density: 0.95-0.954
Additives
HD-52505:
Thermal Antioaxidant (Process Stabilizer)
Catalyst neutralizer(acid scavenger, lubricant)
HD-52505 UV:
Thermal Antioxidant (process Stabilizer)
Antiblocking Agent
Catalyst neutralizer (acid scavenger, lubricant)
UV Stabilizer
Resin Properties | Unit | Typical Value | Test Method |
---|---|---|---|
Melt Index (190°C/ 2.16KG) | g/10 min | 5 | D1238 |
Density | g/cm³ | 0.952 | D1505 |
Thermal Properties | Unit | Typical Value | Test Method |
Vicat Softening Point | °C | 124 | D1525 |
Molded Properties | Unit | Typical Value | Test Method |
Flectural Modulus | Mpa | 1200 | D790 |
Tensile Strength at Yield | Mpa | 27 | D638 |
Tensile Strength at Break | Mpa | 13 | D638 |
H.D.T | °C | 67 | D648 |
Notched Izod Impact @ 23°C | J/m | 29 | D256/A |
HD52518
HDPE made via Spherilene Gas-Phase Technology
52518 is a HDPE copolymer for injection Maudling for applications requiring a good balance between easy of processability and flowability and mechanical properties.
HDPE: HD52518
Characteristic Properties
Good balance between easy of processability and flowability
Density: 0.950-0.954
Main Applications
Housewares
High fluidity
Injection moulding
Density: 0.950-0.954
Additives
Thermal Antioxidant (process Stabilizer)
Catalyst neutralizer (acid scavenger, lubricant)
Ressin Properties | Unit | Typical Value | ASTM Method |
---|---|---|---|
Melt Index (190°C/ 2.16Kg) | g/10 min | 18 | D1238 |
Density | g/ml | 0.952 | D1505 |
Thermal Properties | Unit | Typical Value | Test Method |
Vicat Softening Point | °C | 121 | D1525 |
Moulded Properties @ | Unit | Typical Value | Test Method |
Flexural Modulus | MPa | 1200 | D790 |
Notched Izod Impact @ 23° C | J/m | 19 | D256/A |
HDPE made via Hostalen
HF-4760(BL3) is a blow molding grade resin with high density polyethylenee with 1-Butene as co monomer which is manufactured by the suspension polymerization of ethylene monomer. Stifness, good ESCR are it's spetial properties. High rigidity and good flowability which made it proper for usage in bottles and small blow molding goods.
HDPE: HF-4760(BL3)
Characteristic Properties
High density and stiffness
Good flowability and impact Strength
Good Stress Cracking resistance
Density: 0.952-0.956 g/cm3
Main Applications
For container with capacities ranging from a few ml up to 10 Liters, also for production of sheets for thermoforming.
Density: 0.952-0.956 g/cm3
Additives
Antioxidant/Process stabilizer
Lubricant/ acid scavenger
Resin Properties | Unit | Typical Value | Test Method |
---|---|---|---|
Melt Index(21.6) | g/10 min | 23 | ISO 1133 |
Melt Index(5) | g/10 min | 1.2 | ISO 1133 |
FRR (21.6/5) | - | 19 | - |
Density | g/cm³ | 0.954 | ISO 1183 |
Molded Properties | Unit | Typical Value | Test Method |
Notched Impact @ 23°C | mJ/mm² | 9 | ISO 179/ 1 eA |
HM9450F (EX5)
HDPE: HM9450F (EX5)
HM-9450F (EX5) is blown film grade resin which is manufacture(EX5) is a bi-model high density polyethylene with 1-Butene as co monomer
HDPE: HM9450F (EX5)
Characteristic Properties
High molar mass film grade
Good stiffness and tenacity
Density: 0.947-0.951 g/cm3
Main Applications
For blown films with paper like quality, suitable for counter bags, carrier bags and wrapping films.
Excellent processing.
Density: 0.947-0.951 g/cm3
Additives
Antioxidant/Process stabilizer
Lubricant/ acid scavenger
Test/Composition | Typical Value | Unit | ASTM Method |
---|---|---|---|
Density | 0.949 | g/cm3 | ISO 1183 |
Fish Eye Note | <3 | note | Internal |
FRR 21.6/5 | 29 | h | |
MFR 190°/21.6 | 8.0 | g/10 min | ISO 1133 |
MFR 190°/5 | 0.28 | g/10 min | ISO 1133 |